Abstract The Brazilian Buriti oil presents low extraction costs and relevant antioxidant properties. Thus, this work aimed to analyze Buriti oil biomaterial (BB), within its physicochemical properties, biocompatibility and cellular integration, with the purpose to the use as a growth matrix for Goat Wharton’s jelly mesenchymal stem cells. Biomaterials were produced from Buriti oil polymer (Mauritia flexuosa), for it’s characterization were performed Infrared Region Spectroscopy (FTIR) and Thermogravimetric Analysis (TG and DTG). The biointegration was analyzed by Scanning Electron Microscopy (SEM) and histological techniques. In order to investigate biocompatibility, MTT (3-(4,5-dimetil-2-tiazolil)-2,5-difenil-2H-tetrazólio) test and hemolytic activity tests were performed. The activation capacity of immune system cellswas measured by phagocytic capacity assay and nitric oxide synthesis . The BB presented an amorphous composition, with high thermal stability and high water expansion capacity, a surface with micro and macropores, and good adhesion of Wharton’s jelly mesenchymal stem cells (MSCWJ). We verified the absence of cytotoxicity and hemolytic activity, in addition, BB did not stimulate the activation of macrophages. Proving to be a safe material for direct cultivation and also for manufacturing of compounds used for in vivo applications.

Abstract To analyze the biocompatibility of the scaffold produced from a natural polymer derived from castor oil through hemolytic activity and antimicrobial activity, to enable the clinical application. Three in vitro tests were performed: Hemolytic activity test - Polymer partially dissolved in contact with blood agar; Hemolytic activity test in sheep's blood - Polymer extract with red blood cells solution; Antimicrobial activity test - Solid polymer in direct contact with E. Coli and S. Aureus. For hemolytic tests, none of the samples showed hemolysis. Negative hemolytic activity is a good indicator, as the maintenance of the blood clot in the area of the lesion is essential for the formation of new tissue. For the antimicrobial activity test, no significant activity was observed against the bacteria used. The polymer is not toxic to red blood cells, being viable for clinical application as a matrix for tissue regeneration.

Abstract To analyze the surface topography and mechanical properties of a polyurethane derived from castor oil reinforced with hydroxyapatite (PU–HA) for bone fixation. The surface analysis was performed by Scanning Electron Microscopy (SEM) and the mechanical properties by Vickers microhardness and tensile tests. The SEM images showed that the PU surface presented important characteristics for materials intended for bone fixation, such as an irregular and porous surface. The analysis showed a surface with alternating areas with depressions and elevations of approximately 80±100 µm, presence of pores of 12 µm in size. The microhardness analysis showed values of 0.42±1.01 HV for PU–HA plates, lower in relation to the poly lactic-co-glycolic acid (PLGA) plate (control group). The elastic modulus and ultimate tensile strength of 317.4 MPa, and 35.57 MPa for PLGA sample, 1.187 MPa, and 0.29 MPa for PU–HA sample. The PU produced showed good surface properties, however demands better mechanical properties.

Abstract To produce polysaccharide-based hydrogels and cerium (Ce3+) doped hydroxyapatite plus chitosan and collagen to enable future applications in the treatment of joint degeneration. Hydrogel production and characterization were performed with Fourier transform infrared spectroscopy (FTIR), thermogravimetry analysis (TGA) and cytotoxicity testing with MTT [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide]. A final biomaterial composition was Kelcogel® Gelana (58%), chitosan (22.3%), Ce3+ doped hydroxyapatite (10.7%) and bovine collagen (9%), or selected aspect material gelatinous physical color with whitish color and can be injected. The biomaterial composition was proven in the FTIR and TGA, which also provided the maximum supported temperature. In the MTT assay, despite the reduction in viability of the experimental group compared to the control group, cell viability remained approximately 90%. In the FTIR and TGA tests, the material composition was proven. The material does not present cytotoxic behavior for the MTT test, being an alternative for the treatment of joint diseases.

Abstract Bone fractures to be corrected need stabilization of their extremities, which is achieved with the use of plates and screws. This research aimed to produce castor bean polyurethane (Ricinus communis), to make resorbable plate, structural and thermal analysis. The production was made by the glycerolysis of the triglycerides present in the oil, after addition of polyol/glycerol and hexamethylene diisocyanate (HDI) to form urethane structures, with and without addition of hydroxyapatite. The characterization was by FTIR spectroscopy, scanning electron microscopy (SEM), X-ray diffraction, differential scanning calorimetry and thermogravimetry. Plates with dimensions of 40 mm X 10 mm X 2 mm were obtained. The SEM showed flat and homogeneous surface. DRX analysis showed the semi-crystallinity of the biomaterial. Glass transition and thermal stability up to 50 °C were observed, followed by thermal decomposition up to 450 °C. The produced polyurethane showed it is possible to be applied in the manufacture of plate.